Multilayer Zirconia Dental Block High Strength 1200Mpa
$88.00 – $200.00
High strength 1200Mpa Muti-layer zirconia block.
CAD/CAM System: Open system, Amann Girrbach, Zirkon Zahn,
Shade: Vita 16 colors.
Feature:
- Six layers transitional gradient color seamless from the enamel layer to the body dentin layer
- Great aesthetic translucency: 49% at incisal to 40% at cervical,
- Nature and high bending strength-600 Mpa in incisal to 1200 Mpa in the cervical region
Description
3D High Strength Multilayer Dental Zirconia
The high strength multi-layered zirconia design is meant to resemble the natural shade gradient seen in teeth. The white zirconia base is coated with porcelain to match the final restoration.
Computer-aided design or computer-aided manufacturing technology is utilized to develop and mill the porcelain fused with zirconia crowns. When opposed to layered zirconia, monolithic zirconia generates reduced tooth wear. When compared to unpolished unglazed monolithic zirconia and polished glazed monolithic zirconia, polished unglazed monolithic zirconia showed fewer teeth wear.
Feature
- From the incisal to the cervix, it has a transparency of 40-49 percent.
- From the incisal to the cervix, bending strength is 600-1200 MPA.
- Six layers transition in nature.
- Shade: Vita 16 plus blench BL1,BL2,BL3,BL4.
High strength multilayer zirconia dental blocks are application of bridge, crown, implant, veneer, and most idea for posterior crown due to high bending strength that reach to 1200Mpa.
3D High Strength Multilayer Dental Zirconia is unique for the posterior zirconium restoration.
Dentistry zirconia material chemical composition.
Sintering chart
Additional information
| CAD/CAM System | 98 mm Open System, Amann Girrbach, Zirkon zahn |
|---|---|
| Blank height | 10 mm, 12 mm, 14 mm, 16 mm, 18 mm, 20 mm, 22 mm, 25 mm |
| Colors | A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4 |